Description: Indoor and outdoor rendering and levelling mortar walls, floors and ceilings in thickness from 1 to 5 mm
Binder: Portland Cement
Appearance: Grey powder
Mixing Ratio: 4,5-4,8 lt water / 20 kg powder
Packaging: Packed in 20 kg multi-ply paper bags.
Storage: Store in dry medium. Do not stack more than 10 bags on top of each other.
Shelf Life: 12 months when stored in the original sealed packing in dry place
Pot Life: Approx. 1 hours
Working Time: 25 minutes
Waiting Time: Before Bonding: 6 hours
Application Temperature Range: (+5°C) - (+35°C)
Quality Documents: Non-structural repair mortar conforming
|PREPARATION & APPLICATION|
Preparation:Substrates must be compact, free of dust, loose parts and clean from oils, grease, paint or adhesive residues when YAPFﾝX Thin Repairing Mortar can be applied to damp surfaces without cure time will be slightly prolonged.
Mixing: Pour 20 kg of YAPFIX Coarse Repairing Mortar into 5.5-6 litres of clean water slowly and mix to obtain a homogeneous paste free from lumps. (A low speed mixer is recommended to mix).Allow to stand for 5-10 minutes to mature. After remixing, the paste is ready for application.
Application: Apply YAPFIX CoarseRepairing Mortar with rendering machine flat trowel with a firm pressure to ensure a good adhesion. When applying on walls directly exposed to sun or wind, it is advisable to wet the surface of YAPFﾝX Coarse Repairing for the following 24 hours after application. For surfaces having ideal humidity and in ideal weather conditions, wait for 6 hours before tiling. Waiting time will be shorter in summer and longer in winter conditions. The mortar should be used within 25 minutes. Unfavorable climatic conditions like high temperature, low humidity, wind may shorten this duration. Dispose mortars of which pot life is expired. Clean tools and hands with water, surfaces with a damp cloth
Warnings: Since contains cement, irritating to eyes, respiratory system and skin. Indicated consumption is a general information. It may change depending on the application conditions and surface properties.